Sabre - commercial entrance floor mat

130 Sabre Entrance Mats are smooth surface carpet like mats that are low profile to clear narrow doorways. Material is meant for light to medium foot traffic. Mat contains Delcalon which is a higher denier polypropylene yarn that holds its structure, appearance and is one e of the best wear resistant materials there is for matting. Delcalon is also one of the best in moisture retention and dries quickly. It is 5/16” thick mat ideal for narrow low profile doorways. It is threaded with 19 ounces of tufted cut pile Delcoln yarn every nine square feet with flat vinyl borders to complete the mats look. Vinyl backing ensures the mat will not move. Sabre is available in seven color options sure to fit any décor. Standard sizes that ship the fastest are below – typical turnaround time for standard sizes is 1-2 weeks from the date of order. Custom sizes will need an additional week or two (no more than 4 weeks.)

130 Sabre Entrance mats are a step above the typical commodity mats and are a great choice for a standalone mat for your indoor entrance ways, long aisle, lobbies, or any area where there is light to medium foot traffic, even if traffic is multi-directional. All NoTrax products are easily maintained, some suggestions are below.

130 Sabre Entrance Mats (NoTrax products) have been independently tested in the following conditions yielding positive results.
• Flammability (ASTM D2859, CPSC FF 1-70) Measuring the mats response as an ignition source within a controlled environment. To pass, the un-charred area must be greater than one inch. Mat Results were 3.6 Inches; Note - Passes Federal Flammability Study (DOC FF 1-70.)
• Accelerated Wear: an action of rollers with a specified load. Every sample was rotated ten degrees after every pass. Measured by thickness loss which testing resulted in a 32.30% loss.
• Accelerated Soiling (ASTM D6540-00): for a predetermined length of time the test piece was subjected to an accelerated soiling process. The sample was vacuumed – rated – submitted to an extraction device and then rated again. Results were based on a visually inspection – vacuum rating of 3; 5 Rating after Extraction.
• Water Retention: Sample piece was submerged for five minutes in water, removed - drained for fifteen seconds and weighed. Measured in/for weight gain (gallons per square yard) with results of .42
• Abrasion Resistance (ASTM D3884-01): was done by rubbing two wheels across the surface in a controlled yet wear-away fashion. The results were measured by grams, which was a weight loss of 1.17 grams per test specimen.